The effect of iron oxide on sulfide capacities of CaO-based molten slags

Removing sulfur and phosphorus from molten iron can be expressed by the following reactions, respectively. [S]Fe + (O2-)slag = (S2-)slag + [O]Fe [P]Fe + (3/2) (O2-)slag + (5/2) (FeO)slag = (PO43-)slag + (5/2) Fe(liquid) These equations indicate that desulfurisation and dephosphorisation have opposite oxygen potential conditions. If a small amount of desulfurisation slag not removed is carried over to dephosphorisation process, the reaction of sulfur mentioned above proceeds toward left hand resulting in increasing sulfur content in molten iron. For better understanding of such re-sulfurisation reaction in hot metal pre-treatments, the present study aimed at evaluating the effect of iron oxide on the sulfur distribution ratio between slag and hot metal. To measure sulfide capacities and FeO activities simultaneously at temperatures below the melting point of pure iron, CaO-SiO2-FeO and CaO-Al2O3-FeO ternary molten slags were brought into equilibria with copper-iron-sulfur liquid alloys, and the equilibrium oxygen partial pressures were determined with an electrochemical technique involving the stabilised zirconia solid electrolyte. The experimental results showed that the sulfide capacity increased with an increase in FeO content, and this trend was consistent with the fact that FeO was basic. Although the addition of FeO raised the FeO activity and oxygen potential, the calculated value for sulfur distribution ratio between slag and hot metal increased with increasing FeO content.
Return to parent product
  • The effect of iron oxide on sulfide capacities of CaO-based molten slags
    PDF
    This product is exclusive to Digital library subscription
  • The effect of iron oxide on sulfide capacities of CaO-based molten slags
    PDF
    Normal price $22.00
    Member price from $0.00
    Add to cart

    Fees above are GST inclusive

PD Hours
Approved activity
  • Published: 2024
  • Unique ID: P-04081-W3Q1Q4

Our site uses cookies

We use these to improve your browser experience. By continuing to use the website you agree to the use of cookies.