The main constituents of ferromanganese slags are silicates of Mn, Ca and AI. Factors affecting the recovery of manganese from a low manganese content ferromanganese slag (about 16 per cent MnO) during acid leaching were studied. These included time, temperature, agitation, sulphuric acid addition, solid:liquid ratio and particle size. Agitation rates greater than 300 rev/min. leaching periods greater than 30 min and temperatures above ambient were found to have no effect on Mn recovery. Dissolution of Mn was found to be highly dependent on the amount of acid added.About 90 per cent of the Mn was recovered when 55 times the stoichiometric amount of acid was used. About 28 per cent of the Mn was recovered when the stoichiometric quantity of acid (with respect to Mn alone) was used. However, the recovery increased to about 75 per cent when the total stoichiometric requirement of acid with respect to Ca, Al, Mg and Fe as well as Mn was used for leaching. The extent of Mn dissolution also depended on the particle size of the slag. The percentage of Mn recovery (using 55 times the stoichiometric amount of acid) increased from about 60 per cent to about 92 per cent when particle size decreased from -36 +52 to -150 +200 mesh (B.S.S.). When the results of this study were compared with those in a previous study involv,ing the leaching of a high manganese content slag (containing about 40 per cent MnO) results were similar except that there was a gr-eater consumption of acid in the present case (i.e. low manganese content slag).