A low grade middling sample from Mount Isa, Australia, assaying 31.7 per cent zinc, 12.9 per cent lead and 14.5 per cent iron was leached under atmospheric pressure in sulphate and sulphate-chloride solutions with ferric ions as oxidants. About 96 per cent of the contained zinc was dissolved into a 0.5 M H2SO4 - 0.5 M Fe2(SO4)3 solution at 90C within three hours from a five per cent by weight slurry density mixture. The leaching process is very temperature-dependent, suggesting a surface chemical control. In the latter stage, the leaching rates levelled off and the leaching was most probably controlled by both surface chemical reaction and diffusion processes. The addition of chloride ions in the leach solution resulted in an increase in the leaching rate. About 95 per cent of the lead sulphide contained was converted to lead sulphate which precipitated and remained in the residue. Essentially no lead remained in solution and the low chloride concentration did not affect the precipitation of lead sulphate. Half of the iron orginally present remained in the residue as pyrite although essentially all the cadmium and 90 per cent of the copper initially present were dissolved. Some three per cent of sulphide sulphur was oxidised through to sulphate, about 67 per cent was converted to elemental sulphur which can be recovered by solvent extraction, the rest remained in the residue mainly as pyrite. Ferric sulphate and sulphate-chloride solutions can be used to effectively leach finely ground lead-zinc middlings and other bulk sulphide concentrates. A complete separation of zinc from lead and silver has been demonstrated.