Upgrading of Indonesia's Bauxite by Washing Method There were eight bauxite samples used in this research, three samples from Kijang contain total SiO2 18.36-29.16 per cent, Al2O3 40.12-48.36 per cent, Fe2O3 4.27-5.13 per cent, one sample from Tayan, contains total SiO2 4.69 per cent, Al2O3 38.95 per cent, and Fe2O3 19.67 per cent, and four samples from Mempawah contain total SiO2 33.5-44.8 per cent, Al2O3 29.8-35.9 per cent, Fe2O3 7.29-9.88per cent. All of those bauxite ores have not fulfilled the requirement for Bayer process yet; therefore simple up-grading using a rotary drum scrubber is needed. The scrubbing process was carried out with time variable up to 60 minutes with solid percentage applied was 50 per cent and rotary speed was set up 30 rev/min. The bauxite was washed by following steps: scrubbing, screening, drying, and finally it was analysed to show chemical content. The washed bauxite produced has size fraction that is retained on the 1.7 mm of screen opening. The result of the research shows that the higher alumina content of the raw bauxite, the longer washing time is needed moreover the higher quality of the washed bauxite is produced. The highest alumina content of the washed bauxite was 53.67 per cent with the alumina recovery was 89.66 per cent and the concentration ratio of 84.80 per cent was achieved within 20 minutes of washing time of the raw bauxite (Al2O3 48.36 per cent). The washed bauxite resulted from this research is suitable as a raw material for Bayer process.